Journal of Materials Science Research and Reviews

Physical and Mechanical Properties of Geopolymer Synthesized from Alternate Source Laterite

K. D. Oluborode

Department of Civil Engineering, Federal Polytechnic, Ado – Ekiti, Nigeria.

K. B. Yunus *

Department of Civil Engineering, Federal Polytechnic, Ado – Ekiti, Nigeria.

D. S. Oluborode

Department of Civil Engineering, Federal Polytechnic, Ado – Ekiti, Nigeria.

*Author to whom correspondence should be addressed.

---

Abstract

Procurement and development of materials are essential facts of structural engineering practice. This study seeks to understand potential of laterite deposit in Ado-Ekiti metropolis for development as source material for geopolymer for engineering applications. Scooped laterite from alternate sources of Ekiti Parapo Pavilion and Federal Polytechnic Gate deposits were calcined at 750°c thereafter pulverized. The metallic oxide of the pulverized samples were determined. Alkaline activator solution of NaOH and NaSi0₃ while maintaining NaoH at 8M, with sodium hydroxide - sodium silicate- sterile water ratio of 7:3:3. The alkaline activator with the source material at ratio of 0.45 mixed was used to produce 50×50×50mm³ specimen cubes based on the alternate geopolymer source materials. Sets of the specimen were cured respectively at 27°C (room temperature), oven temperature 50°C and 90°C respectively for 28days, 72hours and 72hours. To evaluate physical and mechanical properties of the specimens, density, porosity and comprehensive strength of the specimens were determined. Result shows that the specimen density decreases with increase of cure temperature while porosity increases with increase cure temperature. Specimen density ranges from 2.16g/cm³-2.4g/cm³ and Porosity ranges from 8.8%-17.64%. Specimen comprehensive strength increases with cure temperature with strength value ranges from 1.74N/mm³-7.24N/mm³ for geopolymer based on Ekiti parapo laterite. The trend for density, porosity and comprehensive strength for the specimen were similar for geopolymer based on the Polytechnic Gate laterite except that the comprehensive strength were relatively lower with minimum value ranges from 0.58N/mm³- 3.80N/mm³.

Keywords: Geopolymer, material, density, porosity, strength

---

---

---

References

Gagg C. Cement and Concrete as an engineering material: an historic appraisal and case study analysis. Engineering Failure Analysis; 2014. DOI:40.10.1016/j.engfailanal.2014.02.004.

Kamal N, Des C, Paul K. High-Strength Geopolymer Concrete- Properties, Advantages and Challenges. Advances in Materials. 2018;7(2):15-25. DOI: 10.11648/j.am.20180702.11

Orji BO, Igbokwe GE, Anagonye CO, Modo EU. Chemical content of the periwinkle shell and its suitability in thin layer chromatography. International Journal of Chemistry Studies. 2017;(1): 09-11.

Raijiwala DB, Patil HS. Geopolymer Concrete: A Green Concrete. 2nd International Conference on Chemical, Biological and Environmental Engineering (ICBEE 2010), 2010 2-4 November, Cairo, Egypt. 2010;202-206.

Rajini B, Narasimha Rao AV. Mechanical properties of geopolymer concrete with fly ash and GGBS as source materials. International Journal of Innovative Research in Science, Engineering, and Technology. 2014;3(9):15944- 15953.

Matsimbe J, Dinka M, Olukanni D, Musonda I, Geopolymer: A Systematic Review of Methodologies. Materials. 2022;15:6852.

Available: https://doi.org/10.3390/ ma15196852.

Matsimbe J, Dinka M, Olukanni D, Musonda I. A Bibliometric Analysis of Research Trends in Geopolymer. Materials. 2022;15:6979. Available:https://doi.org/10.3390/ma15196979.

Cong P, Cheng Y. Advances In Geopolymer Materials: A Comprehensive Review. Journal of Traffic And Transportation Engineering (English Edition). 2021;8 (3):283-314.

Oke OL, Ayeni IS. Effects of Source Materials on Mechanical Properties of Geopolymer Concrete. American Journal of Engineering Research (AJER). 2019; (03):146-150.

Sathawane SH, Vikrant S, Vairagade, Kavita SK. Combine Effect on rice husk ash and fly ash on concrete by 30% cement replacement. Procedia Engineering, Elsevier. 2013;51: 35-44. Available:https://doi.org/10.1016/j.proeng.2013.01.009

Abdullah MMA, Hussin K, Bnhussain M, Ismail KN, Ibrahim WMW. Mechanism and chemical reaction of fly ash geopolymer cement. International Journal of Pure and Applied Sciences and Technology. 2011; 1(6):35-44.

Nikoloutsopoulos N, Sotiropoulou A, Kakali G, Tsivilis S. Physical and Mechanical Properties of Fly Ash Based Geopolymer Concrete Compared to Conventional Concrete. Buildings. 2021;11:178. Available:https://doi.org/10.3390/buildings/11050178